Reciprocating wear behavior of mild steel carburized using Na₂CO₃-NaCl

Liew , Willey Yun Hsien and Roonie Protasius , and Ling , Jester L. J and Nancy Julius Siambun, and Noor Ajian Mohd Lair, (2016) Reciprocating wear behavior of mild steel carburized using Na₂CO₃-NaCl. Tribology International , 95 . pp. 406-418. ISSN 0301-679X

[img]
Preview
PDF
52Kb

Official URL: http://dx.doi.org/10.1016/j.triboint.2015.11.040

Abstract

Abstract The surface of the mild steel carburized using Na2CO3-NaCl was dominated by retained austenite. Towards the core, the amount of austenite reduced while the amount of martensite increased. Increasing the duration of the carburization resulted in higher peak hardness and case depth. It also increased the amount of cementite in the grain boundaries and the austenite grains size, rendering the steel more susceptible to cracking. The superior wear resistance of the martensite, as compared to the austenite, could be attributed to its high cracking and adhesive wear resistance owing to its high hardness and tendency to form oxides. The friction was governed by the wear mechanism and the type of microstructure at the worn scar sliding on the carbide ball.

Item Type:Article
Uncontrolled Keywords:Friction, Microstructure, Mild steel, Wear
Subjects:T Technology > TA Engineering (General). Civil engineering (General)
Divisions:FACULTY > Faculty of Engineering
ID Code:13984
Deposited By:IR Admin
Deposited On:29 Aug 2016 15:50
Last Modified:29 Aug 2016 15:50

Repository Staff Only: item control page


Browse Repository
Collection
   Articles
   Book
   Speeches
   Thesis
   UMS News
Search
Quick Search

   Latest Repository

Link to other Malaysia University Institutional Repository

Malaysia University Institutional Repository