Abdullah Chik, and Nazli Ahmad Aini, and Haider F. Abdul Amir , (2014) Physical characteristic of Zn doped soft ferrites MxZn 1-x Fe2O4. Key Engineering Materials, 594-595 . pp. 39-43. ISSN 10139826
Official URL: http://dx.doi.org/10.4028/www.scientific.net/KEM.5...
The chemical composition and preparation methods for ferrite were studied in order to control the quality of ferrite such as higher initial permeability and low energy losses. Nine samples of soft ferrite MxZn 1-xFe2O4 with M=Ni, Mg, Cu ; x=0.2, 0.3, and 0.4 was prepared using solid state ceramic method and characterized for initial permeability, coercivity and relative loss factor (RLF). Studies show that samples with low Zn concentration, x=0.4, exhibit higher initial permeability, μi, with magnitude highest in sample with Ni concentration, that also has the highest atomic susceptibility among Ni, Mg and Cu. Initial permeability, μi ,also influences the resistivity of the samples with increasing susceptibility of magnetic spins, so samples with higher μi, e.g. Ni0.4Zn0.6Fe2O4 exhibit increased resistivity with increased initial permeability while Cu0.4Zn 0.6Fe2O4 exhibit decreasing resistivity with increasing Cu content and lower initial permeability.
|Uncontrolled Keywords:||Atomic susceptibility, Chemical compositions, Initial permeability, Magnetic spin, Physical characteristics, Preparation method, Soft ferrite, Solid state ceramic method, Energy dissipation,Ferrite, Ferrites, Nickelx|
|Subjects:||T Technology > TA Engineering (General). Civil engineering (General)|
|Deposited By:||IR Admin|
|Deposited On:||15 Jul 2014 08:47|
|Last Modified:||17 Feb 2015 11:17|
Repository Staff Only: item control page