Synthesis Of Bismaleimide-Diaminepolymermatrix In The Presence Of Dicumyl Peroxide: Reaction, Curing Profile And Thermal Properties

Coswald Stephen Sipaut @ Mohd Nasri and Rachel Fran Mansa and Jedol Dayou (2014) Synthesis Of Bismaleimide-Diaminepolymermatrix In The Presence Of Dicumyl Peroxide: Reaction, Curing Profile And Thermal Properties. (Submitted)

[img] Text
Synthesis Of Bismaleimide-Diaminepolymermatrix In The Presence Of Dicumyl Peroxide 24pages.pdf

Download (981kB)
[img] Text
Synthesis Of Bismaleimide-Diaminepolymermatrix In The Presence Of Dicumyl Peroxide Reaction, Curing Profile And Thermal Properties.pdf
Restricted to Registered users only

Download (1MB)

Abstract

The main aim of this study was to develop an improved method for the preparation of a bismaleimide-diamine (BMI/DDM) polymer matrix, achieving shorter curing time, longer processing time (pot life), and good thermal mechanical properties. A matrix of BMI/DDM thermoset was prepared at optimal conditions and formulation, containing BMI and DDM in a 2: 1 mol ratio with 0.1wt% of dicumyl peroxide (DCP) as the curing accelerator. An optimal temperature of 150°C was selected for both melt-mixing and curing processes. The mechanism of matrix preparation was also investigated using differential scanning calorimetry and quantitative Fourier transformed infrared analysis. DCP at the optimal concentration was found to accelerate cross-linking reactions between BMI and DDM without inhibiting the chain-­extension reaction of BMI. The specified formulation exhibited longer gel time (208 s/g) and shorter postcuring time (2 h) compared to other formulations. In addition, thermomechanical behavior and thermal stability were analyzed by dynamic mechanical analysis and thermomechanical analysis, and thermogravimetric analysis, respectively. The storage modulus (E'), glass transition temperature (T9), and decomposition temperature (Td) of the BMI/DDM thermosets increased with the BMI content of the formulations, while the coefficient of thermal expansion and damping behavior (tan o) decreased in a similar manner, primarily because of an increase in the degree of crosslinking.

Item Type: Research Report
Keyword: Bismaleimide-diamine (BMI/DDM) polymer matrix , Dicumyl peroxide , DCP
Subjects: T Technology > TP Chemical technology > TP1-1185 Chemical technology > TP155-156 Chemical engineering
Department: FACULTY > Faculty of Engineering
Depositing User: NORAINI LABUK -
Date Deposited: 14 Oct 2021 09:11
Last Modified: 14 Oct 2021 10:08
URI: https://eprints.ums.edu.my/id/eprint/30849