A systematic investigation of the tribological behaviour of oxides formed on AlSiTiN, CrAlTiN, and CrAlSiTiN coatings

Lim, Hooi Peng and Jiang, Zhong-Tao and Gan, Melvin Jet Hong and Nafarizal Nayan and Chee, Fuei Pien and Soon, Chin Fhong and Naveed Hassan and Liew, Willey Yun Hsien (2022) A systematic investigation of the tribological behaviour of oxides formed on AlSiTiN, CrAlTiN, and CrAlSiTiN coatings. Wear, 512-513. pp. 1-21. ISSN 0043-1648

[img] Text
FULL TEXT.pdf
Restricted to Registered users only

Download (23MB) | Request a copy

Abstract

Changes with temperature in the microstructure and oxide formation of AlSiTiN, CrAlTiN, and CrAlSiTiN coatings were systematically studied using various characterisation techniques. By correlating these results with their tribological behaviour seen in the reciprocating sliding tests, it was concluded that SiO2 was more lubricous than Cr2O3, and provided better wear protection. Although an increase in the amount of SiO2 produced in the tribo-layer resulted in a greater lubricating effect, Cr2O3 produced a much lesser of such benefit. The effect of SiO2 as lubricant was also seen in machining. In the machining of stainless steel at 100 m/min, where flank and notch wear was due to abrasion and mechanical cracking, the CrAlSiTiN coated tools with the highest hardness, H/E, and H3/E2 exhibited the highest wear resistance. However, AlSiTiN coated tools demonstrated reduced flank wear and the lowest wear in machining at 200 m/min. The formation of SiO2 could account for this low level of wear.

Item Type: Article
Keyword: Annealing, Friction, Oxidation, Wear
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA1-2040 Engineering (General). Civil engineering (General) > TA401-492 Materials of engineering and construction. Mechanics of materials
T Technology > TJ Mechanical engineering and machinery > TJ1-1570 Mechanical engineering and machinery > TJ1040-1119 Machinery exclusive of prime movers
Department: FACULTY > Faculty of Engineering
Depositing User: SITI AZIZAH BINTI IDRIS -
Date Deposited: 03 Jul 2025 15:40
Last Modified: 03 Jul 2025 15:40
URI: https://eprints.ums.edu.my/id/eprint/44335

Actions (login required)

View Item View Item