Mohamad Nasir Mohamad Ibrahim and Izat Ezwan and A.R. Wahida and Coswald Stephen Sipaut @ Mohd Nasri (2007) Study on moisture-cured Polyurethane as undercoating layer for Metallization. ASEAN Journal on Science and Technology for Development, 22 (3).

[img]
Preview
Text
Study on moisture cured Polyurethane as undercoating layer for Metallization.pdf

Download (97kB) | Preview

Abstract

In this work a technique of metallizing substrate via electroless plating using moisture-cured polyurethane (MCPU) system as the undercoat is presented. MCPU prepolymer was prepared by mixing polyethylene glycol divinyl ether and diphenylmethane-4, 4’-diisocyanate in 1:1 ratio. The effects of etching time as well as curing period on the surface characteristic of MCPU undercoating were investigated. Contact angle measurements, FTIR and SEM were employed to study the changes on the surface of the treated MCPU undercoatsprior to electroless nickel plating. Electroless plating was performed using nickel bath and visual inspection was performed after completing the electroless plating cycles. Relative increase in wettability of the treated MCPU was observed. The surface became hydrophilic after subjecting to mild etching for 1 minute. SEM analysis revealed different pitted structures on the treated MCPU that were cured at different periods. FTIR analysis of the treated MCPU showed some chemical changes marked by the presence of free hydroxyl group and decrease of CH (methylene), urethane C=O, urethane amide and ether peaks. FTIR also showed the sign of further NCO reaction, which indicates by the decrease of NCO peak and increase of NH and urea C=O peaks. The standard pull-off testing method (ASTM D 4541) was employed to evaluate the adhesion strength of nickel deposits coated on MCPU undercoating layer.The test results revealed that curing period and etching time influence the adhesion performance.The results also show that at a selected curing period, prolong etching time will decrease the adhesion strength. Meanwhile prolong curing period will improve the adhesion strength.

Item Type: Article
Keyword: Electroless plating , moisture-cured polyurethane (MCPU) system , polyethylene glycol divinyl
Subjects: T Technology > TP Chemical technology
Department: FACULTY > Faculty of Engineering
Depositing User: NORAINI LABUK -
Date Deposited: 21 Jun 2018 13:53
Last Modified: 21 Jun 2018 13:53
URI: https://eprints.ums.edu.my/id/eprint/20325

Actions (login required)

View Item View Item