Fauziah Abdul Aziz (2009) Lignin and cellulose wood for Polymeric Electrolyte. (Unpublished)
|
Text
Lignin and cellulose wood for Polymeric Electrolyte.pdf Download (61kB) | Preview |
|
Text
Lignin and cellulose wood for Polymeric Electrolyte.pdf Restricted to Registered users only Download (1MB) |
Abstract
FT-IR Spectroscopy, XPS and XRD works have been used to characterize lignin and cellulose from several hardwoods of Sabah. The FT -IR has revealed that all of the five hardwoods lignin had a common pattern of spectra, but only the Kapur and Belian lignin have shown lower intensities of bands compared to the Keranji, Merbau and Nyatoh lignin between 3460 - 1300 cm region. All lignin have shown a broad band at 34100-3460 cm, attributed to the hydroxyl groups in phenolic and al iphatic structures (OH stretching). Solid polymer electrolytes (SPE) produced using lignin / cellulose sample - was partially dissolved in the THF solvent and prior to blend with ENR-50 rubber. Ionic conductivity measurements at various temperatures were also obtained over the range of 25-80oC. The electrochemical stability of polymer electrolytes were also obtained; impedance measurement were taken for several days. Ionic conductivity were also determined. DSC analyzer was used to determine thermal properties of the polymer electrolyte samples. All samples display a single glass transition temperature, T g. The changes T g values were observed when different weight per cent of Li salt and lignin/cellulose added into the systems
Item Type: | Research Report |
---|---|
Keyword: | Sabah , hardwoods , Solid polymer electrolytes (SPE) |
Subjects: | T Technology > TS Manufactures |
Depositing User: | NORAINI LABUK - |
Date Deposited: | 30 Sep 2019 08:27 |
Last Modified: | 30 Sep 2020 10:57 |
URI: | https://eprints.ums.edu.my/id/eprint/23045 |
Actions (login required)
View Item |