Verra Gulitah and Liew, Kang Chiang (2019) Three different recycle codes of plastic/Acacia fibre composites: physical and morphological properties. International Journal Of Biobased Plastics, 1. pp. 1-7. ISSN 2475-9651
Text
Three different recycle codes of plastic Acacia fibre composites.pdf Download (43kB) |
|
Text
Three different recycle codes of plastic Acacia fibre composites1.pdf Restricted to Registered users only Download (980kB) |
Abstract
In this study, the term wood-plastic composite (WPC) refers to three different recycle codes of plastics combine with Acacia fiber namely polypropylene-wood fiber (PP-WF), high density polyethylene-wood fiber (HDPE-WF), and low-density polyethylene wood fiber (LDPE-WF). Each WPC was produced at different percentage combination (100:0, 90:10, 80:20, 70:30, 60:40, and 50:50). The relationship between plastic content and the physical properties (water absorption, thickness swelling, and density) of WPC were investigated. Water absorption and thickness swelling were evaluated after 15 days of water immersion. It was found that WPC of PP-WF, HDPE-WF and LDPE-WF had a significant difference at P ≤ 0.05 for water absorption, thickness swelling, and density. While water absorption and thickness swelling increased when the plastic content decreased. At combination of 50:50, WPC of PPWF, HDPE-WF, and LDPE-WF showed range value between 52.03% and 56.27% of water absorption. While for thickness swelling at combination of 50:50 WPC of PP-WF showed 4.62%, HDPE-WF and LDPE-WF showed 4.61% and 4.77%, respectively. WPC of PP-WF, HDPE-WF, and LDPE-WF showed density 1.033 g/cm3, 0.862 g/cm3, and 0.870 g/cm3 respectively, at 100% plastic content. This finding revealed due to the present of hydroxyl group in wood fiber and some voids in WPC. The evidence of the poor interfacial bonding in WPC was analyzed using scanning electron microscope.
Item Type: | Article |
---|---|
Keyword: | High density polyethylene , Low density polyethylene , Polypropylene , Physical properties , Plastic content , Wood fibre |
Subjects: | Q Science > Q Science (General) T Technology > TD Environmental technology. Sanitary engineering |
Department: | FACULTY > Faculty of Science and Natural Resources |
Depositing User: | SITI AZIZAH BINTI IDRIS - |
Date Deposited: | 22 Jul 2021 13:53 |
Last Modified: | 22 Jul 2021 13:53 |
URI: | https://eprints.ums.edu.my/id/eprint/30039 |
Actions (login required)
View Item |